Conventional Precision Spindle Oil

Made with refined mineral base oil and fortified with anti-wear, anti-oxidation, anti-corrosion and anti-foam additives. Suitable for machine tool spindles with general precision requirements. Cost-effective and widely used as a general industrial grade.

Synthetic Spindle Oil

Formulated with synthetic base oils such as poly-alpha-olefin (PAO) and esters. Its overall performance is far superior to mineral oil, with better viscosity-temperature characteristics, oxidation resistance, low-temperature fluidity and temperature rise control. Ideal for ultra-high-speed, ultra-high-precision CNC equipment (e.g. 5-axis machining centers, mirror grinders) and suitable for long-term continuous high-speed operation.

General Basic Parameters (Applicable to All Viscosity Grades)

Item  Mineral Spindle Oil Synthetic Spindle Oil (PAO/Ester) Test Standard Core significance
Jenis Minyak Dasar Refined Mineral Oil Polyalphaolefin (PAO)/Ester Synthetic Oil – Determine the basic performance and temperature resistance of the oil.
Sistem Aditif Anti-wear + Anti-oxidation + Anti-corrosion + Anti-foaming High-efficiency Anti-wear + High-temperature Anti-oxidation + Anti-foaming + Rust-proof – Adapt to high-speed and light-load conditions, extend oil service life.
Cleanliness Grade ≥ISO 4406 18/16/13 ≥ISO 4406 15/13/10 ISO 4406 Prevent impurities from clogging precision spindle oil circuits and wearing bearings.
Flash Point (Open Cup) ≥120℃ ≥130℃ GB/T 3536 / ASTM D92 Prevent fire risk caused by temperature rise during high-speed operation.
Titik Tuang ≤-15℃ ≤-30℃ GB/T 3535 / ASTM D97 Ensure lubrication performance during equipment start-up and shutdown in low-temperature environments.
Water-soluble Acid or Alkali None None GB/T 259 / ASTM D974 Prevent corrosion of spindle metal components.
Kotoran Mekanis ≤0.005% ≤0.001% GB/T 511 / ASTM D4057 Avoid scratching the precision surface of bearings.
Moisture ≤0.03% ≤0.01% GB/T 260 / ASTM D95 Prevent bearing rust and oil film rupture.

Core Performance Parameters by Viscosity Grade (40℃)

Mineral Spindle Oil (ISO VG3~15)

Viscosity Grade (ISO VG) Kinematic Viscosity (mm²/s) Indeks Viskositas (VI) Brookfield Viscosity (mPa· s, 20℃) Anti-wear Performance (Wear Scar Diameter, mm) Air Release Value (min, 50℃) Foaming Property (mL/mL, 24℃)
3 2.8~3.2 ≥90 ≤30 ≤0,40 ≤3 ≤100/0
5 4.1~5.6 ≥95 ≤50 ≤0,40 ≤4 ≤100/0
7 6.1~7.4 ≥95 ≤70 ≤0,42 ≤5 ≤150/0
10 9.0~11.0 ≥100 ≤100 ≤0,42 ≤6 ≤150/0
15 13.5~16.5 ≥100 ≤150 ≤0.45 ≤8 ≤200/0

Synthetic Spindle Oil (ISO VG3~15)

Viscosity Grade (ISO VG) Kinematic Viscosity (mm²/s) Indeks Viskositas (VI) Brookfield Viscosity (mPa· s, 20℃) Anti-wear Performance (Wear Scar Diameter, mm) Air Release Value (min,50℃) Foaming Property (mL/mL,24℃)
3 2.8~3.2 ≥140 ≤25 ≤0.35 ≤2 ≤50/0
5 4.1~5.6 ≥140 ≤45 ≤0.35 ≤3 ≤50/0
7 6.1~7.4 ≥150 ≤65 ≤0.38 ≤4 ≤100/0
10 9.0~11.0 ≥150 ≤95 ≤0.38 ≤5 ≤100/0
15 13.5~16.5 ≥150 ≤140 ≤0,40 ≤6 ≤150/0

Supplementary Parameters for Key Performance (High-temperature/Working Condition Adaptation)

Item  Mineral Spindle Oil Synthetic Spindle Oil Test Standard Operating condition adaptation
High-temperature Oxidation Resistance (Rotary Bomb Oxidation Test) ≥150min ≥350min GB/T 12581 / ASTM D2272 Synthetic type is suitable for 24-hour continuous high-speed operation, not easy to generate sludge.
High-temperature Kinematic Viscosity (100℃) VG10≤4.0mm²/s VG10≤3.8mm²/s GB/T 265 / ASTM D445 Better temperature rise control, avoid thermal deformation of high-speed spindle.
Rust-proof Performance (Distilled Water Method) Tanpa Karat Tanpa Karat GB/T 11143 / ASTM D665 Adapt to humid processing environment, protect spindle bearings.
Anti-emulsibility ≤30min (40-37-3) ≤15min (40-37-3) GB/T 7305 / ASTM D1401 Quickly separate a small amount of water ingress, avoid oil film failure.

Working Condition Adaptation Quick Reference

Kelas Viskositas Spindle Speed Adaptable Equipment Keterangan
3/5 ＞8000r/min High-speed Grinder, Nano-level Machining Center, Motor Spindle Synthetic type is preferred for better temperature rise control.
7/10 3000~8000r/min CNC Lathe, Machining Center, Medium-high Speed Milling Machine Mineral type meets general precision, synthetic type is suitable for long-term operation.
15 ＜3000r/min Low-speed Heavy-duty Machine Tool, Light-load Gear in Spindle Box Can also be used for lubrication of light-load hydraulic systems of machine tools.

Spesifikasi Kemasan

  • Small:18L/barel
  • Large: 200L/barrel, 1000L/IBC ton barrel
  • Customizable: LOGO and product information (MOQ negotiable)